Pengaruh Komposisi Penambahan Limbah Plastik LDPE dan Serbuk Sabut Kelapa Terhadap Nilai Densitas dan Kuat Tekan Batako Ringan
Abstract
Research has been carried out which aims to determine the characteristics of lightweight bricks from LDPE plastic waste and coconut fiber powder produced. Variations in the composition of LDPE plastic and coconut fiber powder are 5%:35%, 10%:30%, and 15%:25% with a water cement factor (FAS) value of 0.5 using a hot press machine with a room temperature of 32°C. There is an effect of adding LDPE plastic waste and coconut fiber powder to lightweight bricks. The results of testing brick samples with a variation of 5%:35% produced a density value of 1,316 kg/m3 and produced a compressive strength value of 6.16 MPa which is included in the IA quality level and can be applied as a structural brick for walls exposed to the environment (outdoor). and others who do not bear the heavy loads specified by the SNI 8640:2018 standard..
Downloads
References
T. Landi, “PERANCANGAN DAN UJI ALAT PENGOLAH SAMPAH PLASTIK JENIS LDPE (LOW DENSITY POLYETHYLENE) MENJADI BAHAN BAKAR ALTERNATIF,” vol. 5, no. 1, 2017.
D. A. Al-Ayyubi and F. D. Ikram, “ANALISIS PENGARUH CAMPURAN LIMBAH PLASTIK LOW DENSITY POLYETHYLENE DAN FLY ASH TERHADAP DENSITAS, KUAT TEKAN DAN KONDUKTIVITAS TERMAL SEBAGAI BAHAN ALTERNATIF BATAKO,” vol. 1, no. 1, 2023.
H. Sutrisna, “ANALISIS PENGARUH KOMPOSIT BERBAHAN LIMBAH PLASTIK LOW DENSITY POLYETHYLENE DAN BOTTOM ASH SEBAGAI BAHAN ALTERNATIF BATAKO,” vol. 1, no. 1, 2023.
A. Supriyadi, “PENGUJIAN SIFAT MEKANIS BATAKO PEJAL MENGGUNAKAN GABUS KELAPA DENGAN VARIASI VOLUME GABUS 10%, 15%, 20% DAN 50%”.
A. Supriyadi, “PENGUJIAN SIFAT MEKANIS BATAKO PEJAL DENGAN SERAT KELAPA DENGAN VARIASI 1,5 CM, 2 CM DAN 2,5 CM”.
L. S. Utami, K. Anwar, and M. N. Fadli, “PEMANFAATAN SAMPAH STYROFOAM MENJADI BATAKO RINGAN TAHAN GEMPA,” vol. 7.
H. Syahwanti, I. Irvhaneil, and R. Christiana, “Analisis Karakteristik Serbuk Sabut Kelapa (Cocopeat) Sebagai Agregat Halus pada Campuran Beton,” J. Serambi Eng., vol. 7, no. 1, Dec. 2021, doi: 10.32672/jse.v7i1.3712.
A. A. Wiyogo, “Pemanfaatan Serbuk Sabut Kelapa (Cocopeat) sebagai Bahan Campuran Beton Sederhana,” vol. 01, 2022.
E. Jumiati, “KARAKTERISTIK SIFAT FISIS BATAKO BERBAHAN LIMBAH KERTAS,” J. Ikat. ALUMNI Fis., vol. 7, no. 3, p. 7, Sep. 2021, doi: 10.24114/jiaf.v7i3.27618.
P. Ramadhan, “PENGARUH PENGGUNAAN LIMBAH PLASTIK LDPE SEBAGAI AGREGAT HALUS PADA BATAKO BETON RINGAN”.
I. B. Rahardja, V. N. C. Surbakti, and A. L. Siregar, “EMPOWERING ABU CANGKANG KELAPA SAWIT TERHADAP KUALITAS BATA BETON RINGAN (LIGHT-WEIGHT CONCRETE),” J. Teknol., vol. 14, no. 1, 2022.
L. Ni’mah, I. Syauqiah, A. Mirwan, D. R. Wicakso, and H. Wijayanti, “BATAKO DARI LIMBAH BOTOL PLASTIK : TINJAUAN KUAT TEKAN,” AL ULUM J. SAINS DAN Teknol., vol. 5, no. 1, p. 26, Nov. 2019, doi: 10.31602/ajst.v5i1.2560.
P. Ardhiantika and A. Basuki, “KAJIAN KUAT TEKAN, KUAT TARIK, KUAT LENTUR DAN REDAMAN BUNYI PADA PANEL DINDING BETON RINGAN DENGAN AGREGAT LIMBAH PLASTIK PET”.
M. T. Rochadi, “PENGARUH VARIASI PENAMBAHAN LIMBAH PLASTIK TERHADAP KEKUATAN TEKAN BATAKO DALAM UPAYA PEMANFAATAN LIMBAH,” vol. 23, no. 2, 2018.
Mulyono, Tri. 2021. Bahan Bangunan Dan Konstruksi. Yogyakarta : Stiletto Indie Book.
Copyright (c) 2023 Nurul Safina, Ety Jumiati, Miftahul Husnah
This work is licensed under a Creative Commons Attribution 4.0 International License.