PENGARUH WAKTU PERENDAMAN LAPISAN TIO2 DALAM DYE EKSTRAK DAUN PACAR KUKU TERHADAP NILAI EFISIENSI DSSC
Abstract
This study is about Dye Sensitized Solar Cell (DSSC) which aims to determine the absorbance value of henna leaf extract (Lawsonia Inermis L) as a sensitizer in DSSC and find out how the effect of immersion time of TiO2 layer on the efficiency value produced. The method used to make the extract is maceration and to doping TiO2 using the doctor blade method with an area of 1.5x1.5 cm. In this study UV-Vis testing was carried out to determine the absorbance value of dye henna leaf extract, current and voltage testing to determine the current and voltage values obtained from cells and SEM tests to determine the surface structure of TiO2 layers. The absorbance value of the nail extract leaf extract is based on the results of the UV Vis test which is 0.077 which is located in an area with a wavelength of 663 nm. For the TiO2 coating immersion time obtained the lowest efficiency value of cells with immersion of TiO2 layer for 1 hour which is 0.0038%, then immersion of TiO2 layer for 12 hours obtained efficiency value 0.0056% and soaking TiO2 layer for 24 hours obtained efficiency value 0.0083%.Downloads
References
Ardianto, Rino et al., 2015. Jurnal Keteknikan Pertanian Tropis dan Biosistem. Uji Kinerja Dye Sensitized Solar Cell (DSSC) menggunakan Lapisan Capacitive Touchscreen Sebagai Substrat dan Ekstrak Klorofil Nannochloropsis Sp. sebagai Dye Sensitizer dengan Variasi Ketebalan Pasta TiO2.
Anggraeni, Nuha Desi., 2008. “Analisa SEM (Scanning Electron Microscopy ) dalam Pemantauan Proses Oksidasi Magnetite Menjadi Hematite.” Seminar Nasional - VII Rekayasa dan Aplikasi Teknik Mesin di Industri (October 2014): 50–56.
Alfanz, Rocky et al., 2015. Rancang Bangun Penyedia Energi Listrik Tenaga Hibrida (PLTS- PLTB-PLN) Untuk Membantu Pasokan Listrik Rumah Tinggal. Setrum 4(2): 34–42.
Dwi Fahyuan, Helga, Faizar Farid, and dan Sarina Pakpahan., 2015. 1 JoP Disain Prototipe Sel Surya Dssc (Dye Sensitized Solar Cell) Lapisan Grafit/Tio 2 Berbasis Dye Alami Abstract [Title: Solar Cell Prototype Design Of Dssc (Dye Sensitized Solar Cell) Graphite Coating / Tio2 Based On Natural Dye] A Research on Solar Cells Prototype Design DSSC Layer Graphite / TiO2-Based Natural.
Fitria, Anisa et al., 2016. 3 Jom FTEKNIK Pembuatan Prototip Dye Sensitized Solar Cell (DSSC) Menggunakan Dye Ekstrak Buah Senduduk (Melastoma Malabathricum L) Dengan Variasi Fraksi Pelarut Dan Lama Perendaman Coating TiO2.
Gultom, Togar Timoteus, and Masyarakat Indonesia., 2017. “Pemenuhan Sumber Tenaga Listrik Di Indonesia.” 3(1).
Kristen, Universitas, and Satya Wacana. 2013. “Pembuatan Prototipe.” 4(1): 345–50.
Noly, Ariza, and A Metodologi Penelitian., 2012. “Sintesis Dan Karakterisasi Sifat Magnetik Serbuk Barium M-Heksaferrit Dengan Doping Ion Zn Pada Variasi Temperatur Rendah.” 1(1): 52–54. JFT. No.1, Vol. 6, Juni 2019 46 | JFT.
Rohi, Daniel, and Jandy E.Luik., “Kesadaran Masyarakat Surabaya Untuk Memiliki Gaya Hidup Ramah Lingkungan, Green Living melalui Menghemat Penggunaan Energi Listrik.” : 1–17.
Sujatno, Agus, Rohmad Salam, and Arbi Dimyati Pusat Sains dan Teknologi Bahan Maju., 2015. “Studi Scanning Electron Microscopy (Sem) untuk Karakterisasi Proses Oxidasi Paduan Zirkonium.” Jurnal Forum Nuklir (JFN) 9(2): 44–50.
Teknik, Fakultas, Universitas Negeri Surabaya., 2015. “Pengaruh Konsentrasi Mordan Kapur dengan Zat Warna Daun Pacar Kuku (Lawsonia Inermis) Kering terhadap Pewarnaan Kain Knit Cotton Shella Setiana Juhrah Singke Abstrak.” 04.
Triyati, Oleh Etty., 1985. “Spektrofotometer Ultra-Violet dan Sinar Tampak serta Aplikasinya dalam Oseanologi.” 1(1): 39–47.
W, Soraya Ratna., 2013. “Pembuatan Sediaan Pewarna Rambut dalam Bentuk Gel dari Infus Pacar Kuku.” : 1–12.