UJI KUAT TEKAN DAN KEAUSAN BAHAN KAMPAS REM DARI KOMPOSISI TEMPURUNG KEMIRI DAN SERAT BAMBU
Abstract
This research aims to find out the best composition of brake lining materials from the shell of candlelnut and bamboo fiber through hardness testing and wear and tear of brake lining materials. The method used is direct emphasis using the Universal Testing Machine and Oghosi tools using the High Speed Universal Wear Testing Machine (Type OAT-U) Oghosi tool. Brake lining materials consist of shell powder of candlenut and bamboo fiber and then added aluminum powder and polyester resin with percent of specific composition for each sample. The results of this study were the five samples having lower wear value than the market but only the sample 4 with the composition of 15% of the shell powder of candlenut, 30% bamboo fiber, 15% aluminum powder and 40% polyester resin recommended as alternative material of brake lining because of its hardness close to the hardness of the material of brake lining of the market is 13.5 BHN and its wear is 2,96 x 10-6 mm2 / kg.
Key Words: Strong Test of Pressure, Wear of Brush, Bamboo Fiber, Shell Powder of Candlenut, Aluminium Powder, and ResinDownloads
References
Alu Syaikh, Dr. Abdullah bin Muhammad. Lubaabut Tafsir ibnu katsir. Jilid 5. Pustaka Imam Syafii: Jakarta. 2012.
Amanto, Hari dan Daryanto. Ilmu Bahan. PT. Bumi Aksara: Jakarta.2003.
Asroni dan Deni Nurkholis. Pengaruh Komposisi Resin Poliester Terhadap Kekerasan dan Kekuatan Tarik Komposit Papan Partikel Onggok Limbah Singkong. Jurusan Teknik Mesin. Universitas Muhammadiyah Metro.2016.
Chandra,Adi dan Asroni. Pengaruh Komposisi Resin Polyester Terhadap Kekuatan Bending Komposit Yang Diperkuat Serat Bambu Apus. Jurusan Teknik Mesin Universitas Muhammadiyah Metro.Lampung.2015.
Dwi Haryadi, Gunawan. Dkk. Perlakuan Abu Biji Kapuk Randu Untuk Bahan Kampas Rem Kendaraan Bermotor. Jurusan Teknik Mesin.Fakultas Teknik. Universitas Diponegoro.2014.
Frick,Heinz dan Koesmartadi, Ch. Ilmu Bahan Bangunan (Ekploitasi, Pembuatan, Penggunaan dan Pembuangan). KANISIUS (Anggota IKAPI) Yogyakarta dan SOEGIJAPRANATA UNIVERSITY PRESS. Semarang: Cet.12.1999.
https://ftkceria.wordpress.com/2012/04/28/uji-keausan-wear/ (diakses pada tanggal 21 januari 2018)
Herman, Maman dkk. Prospek Pengembangan Tanaman Kemiri Minyak (Reutealis Trisperma (Blanco) Airy Shaw) Sebagai Sumber Energi Terbarukan. Balai Penelitian Tanaman Industri dan Penyegar: Sukabumi.2013.
Ilmu purboputro,Promuko. Pengembangan Bahan Kampas Rem Sepeda Motor Dari Komposit Serat Bambu Terhadap Ketahanan Aus Pada Kondisi Kering dan Basah. Departement Of Mechanical Engineering Universitas Muhammadiyah Surakarta.2016.
Kiswiranti, D.,dkk. Pemanfaatan Serbuk Tempurung Kelapa Sebagai Alternatif Serat Penguat Bahan Friksi Non-Asbes Pada Kampas Rem Sepeda Motor. Jurusan Fisika, Fakultas Matematika Dan Ilmu Pengetahuan Alam Universitas Negeri Semarang (UNNS): Semarang.2009.
Nieman, G. Elemen Mesin Jilid 1 Desai Dan Kalkulasi Dari Sambungan, Bantalan dan Poros Edisi Kedua Kerjasama Dengan DR.ing M.Hirt. Jakarta: Erlangga.1994.
Nugroho,Eko dan Nasroni. Pengaruh Komposisi Resin Terhadap Kekuatan Mekanik Papan Partikel Yang Diperkuat Serbuk Kayu Akasia. Jurusan Teknik Mesin Fakultas Teknik Universitas Muhammadiyah Metro. Lampung.2016.
Qurahman, Taufik dan Syarifuddin. Analisa Beban Pengereman Terhadap Kualitas Kampas Rem Tromol Mobil dengan Metode Oghosi. Politeknik Harapan Bersama Jurusan Teknik Mesin: Tegal.2016.
S.Yoresta,Fengky. Sifat Mekanis Bambu Betung (Dendrocalamus Asper). Departement Hasil Hutan Fakultas Kehutanan IPB.Bogor.2013.
Shibab, M. Quraish. Tafsir Al-Misbah: Pesan, Kesan dan Keserasian Al-Qura’an Vol 7. Jakarta: Lentera Hati.2002.
Sularso dan Suga, Kiyokatsu. Dasar Perencanaan Dan Pemilihan Elemen Mesin. PT. Pranadya Paramita: Jakarta.1997.
Suparno,Ono. Penghilangan Hemiselulosa Serat Bambu Secara Enzimatik Untuk Pembuatan Serat Bambu. Departement Teknologi Industri Pertanian.Fakultas Teknologi Pertanian IPB. Bogor.2017.
Surdia, Ir. Tata dan Saito, Dr. Shinroku. Pengetahuan Bahan Teknik. Pradnya Paramita: Jakarta.2005.
Sutikno Dkk. Sifat Mekanik Bahan Gesek Rem Komposit Diperkuat Serat Bambu. Jurusan Fisika Fakultas Matematika Dan Ilmu Pengetahuan Alam Universitas Negeri Semarang. Semarang.2012.
Syawaluddin dan Setiawan, Iman Agus. Perbandingan Pengujian Mekanis Terhadap Kampas Rem Asbes dan Non-Asbestos Dengan Melakukan Uji Komposisi, Uji Kekeraan dan Uji Keausan.Teknik Mesin Universitas Muhammadiyah: Jakarta.
Turmuzi, Muhammad. Pengembangan Pori Arang Hasil Pirolisa Tempurung Kemiri. Fakultas Teknik USU Medan.2005.
Yogha pratama, Yudha. Pengaruh Perlakuan Alkali, Fraksi Volume Serat, dan Panjang Serat Serabut Kelapa-Polyester. Jurusan Teknik Industri Universitas Sebelas Maret.2014.2015.