PENGARUH PERBANDINGAN MOLAR OKSIDA SiO2:Al2O3 dan Na2O:SiO2 TERHADAP SIFAT MEKANIK GEOPOLIMER BERBASIS LATERITE DEPOSIT BONE
Abstrak
The main objective of this research is to determine the effect of molar oxides of SiO2:Al2O3 and Na2O:SiO2 to the mechanical properties of geopolymer based on laterite soil deposite Bone. Geopolymers were produced through alkali-activation method of dehydroxylation laterite. Dehydroxylation was performed by using high-temperature furnace at for 4 hours. The chemical compositions and the microstructure properties of the starting and the resulting materials were characterized based on X-Ray Diffraction (XRD) and Scanning Electron Microscopys (SEM). Measurements of bulk density, apparent porosity and compressive strength were carried out by using Archimedes method and Universal Testing Machine. The results showed that the highest phase of the starting material was quartz (SiO2). The physical properties of geopolymers was examined from the value of their bulk density, apparent porosity and the magnitude of their compressive strength. The results showed that the value of the porosity and the density are inversely proportional, the smaller the porosity, the greater the density. The highest compressive strength value was 6.33 MPa obtained from the sample designated as K6. It was found that geopolymer based on Bone laterite exhibited good mechanical properties.
##plugins.generic.usageStats.downloads##
Referensi
Bodian, S., Faye, M., Sene, N. A., Sambou, V., Limam, O., & Thiam, A. (2018). Thermo-mechanical behavior of unfired bricks and fired bricks made from a mixture of clay soil and laterite. Journal of Building Engineering, 18, 172–179. https://doi.org/10.1016/j.jobe.2018.03.014
Kaze, C. R., Djobo, J. N. Y., Nana, A., Tchakoute, H. K., Kamseu, E., Melo, U. C., … Rahier, H. (2018). Effect of silicate modulus on the setting, mechanical strength and microstructure of iron-rich aluminosilicate (laterite) based-geopolymer cured at room temperature. Ceramics International, 44(17), 21442–21450. https://doi.org/10.1016/j.ceramint.2018.08.205
Kaze, C. R., Venyite, P., Nana, A., Juvenal, D. N., Tchakoute, H. K., Rahier, H., … Leonelli, C. (2020). Meta-halloysite to improve compactness in iron-rich laterite-based alkali activated materials. Materials Chemistry and Physics, 239, 122268. https://doi.org/10.1016/j.matchemphys.2019.122268
Kolawole, F. O., Olugbemi, O. M., Kolawole, S. K., Owa, A. F., & Ajayi, E. S. (2017). Fracture Toughness and Strength of Bamboo-Fiber Reinforced Laterite as Building Block Material. Universal Journal of Materials Science, 5(3), 64–72. https://doi.org/10.13189/ujms.2017.050302
Puspitasari, Y., & Atmaja, L. (t.t.). SINTESIS DAN KARAKTERISASI GEOPOLIMER BERDASARKAN VARIASI RASIO MOL SiO2/Al2O3 DARI ABU LAYANG PLTU SURALAYA. 6.
Shojaei, M., Behfarnia, K., & Mohebi, R. (2015). Application of alkali-activated slag concrete in railway sleepers. Materials & Design, 69, 89–95. https://doi.org/10.1016/j.matdes.2014.12.051
Subaer, Amalia, N., Nurfadilla, Riska, A., Sulfiana, & San, F. P. (2017). The Potential of Laterite Soils Deposit South Sulawesi as a Precursor for Na-Poly (Ferro-Sialate) Geopolymers. MATEC Web of Conferences, 97, 01014. https://doi.org/10.1051/matecconf/20179701014
Subaer, Haris, A., Irhamsyah, A., Akifah, N., & Amalia, N. S. (2019). Physico-Mechanical Properties of Geopolymer Based on Laterite Deposit Sidrap, South Sulawesi. Journal of Physics: Conference Series, 1244, 012037. https://doi.org/10.1088/1742-6596/1244/1/012037
Zhang, H. Y., Kodur, V., Wu, B., Cao, L., & Wang, F. (2016). Thermal behavior and mechanical properties of geopolymer mortar after exposure to elevated temperatures. Construction and Building Materials, 109, 17–24. https://doi.org/10.1016/j.conbuildmat.2016.01.043